DIN 17100 St37-2 Steel (Material 1.0037)

St37-2 steel (material 1.0037) is a type of unalloyed structural steel that complies with DIN 17100:1980 and has been phased out since 2004. According to the German standard DIN 17100, St37 steel is divided into St37-2 , USt37-2, RSt37-2 and St37-3. The new St 37 material designation is S235, and the new St37-2 designation is S235JR (1.0038), the new standard is EN 10025-2:2004.

St37 Steel Datasheet and Specifications

The technical sheet and specifications of the St37 material can be found in the following tables.

Chemical composition

The following table shows the chemical composition of material 1.0037.

Technical data sheet for steel 1.0037 – 1, Chemical composition (ladle analysis) in accordance with DIN 17100 and DIN EN 10025:1993.

Country (Region)	Standard	Steel grade (steel number)	W	Mn	P	s	N	Ass	Thickness (d) (mm)	Deoxidation method
Germany	DIN 17100: 1980	St37-2 (1.0037)	0.17		0.050	0.050	0.009		≤ 16	Optional
			0.20						16
		USt37-2 (1.0036)	0.17		0.050	0.050	0.007		≤ 16	Rimming
			0.20						16
		RSt37-2 (1.0038)	0.17		0.050	0.050	0.009		≤ 40	Dead
			0.20						> 40
		St37-3 (1.0116)	0.17		0.040	0.040	–		All	Dead Special
European Union	EN 10025: 1993	S235JR (1.0037)	0.17	1.40	0.045	0.045	0.009		≤ 16	Optional
			0.20						16
	EN 10025-2: 2004	S235JR (1.0038)	0.17	1.40	0.035	0.035	0.012	0.55	≤ 40	Dead
			0.20						> 40

Technical data sheet for steel St37 – 2, Chemical composition (part analysis) according to DIN 17100 and DIN EN 10025: 1993.

			Chemical Composition (product analysis), %, ≤
Country (Region)	Standard	Steel grade (steel number)	W	Mn	P	s	N	Ass	Thickness (d) (mm)	Deoxidation method
Germany	DIN 17100: 1980	St37-2 (1.0037)	0.21		0.065	0.065	0.010		≤ 16	Optional
			0.25						16
		USt37-2 (1.0036)	0.21		0.065	0.065	0.009		≤ 16	Rimming
			0.25						16
		RSt37-2 (1.0038)	0.19		0.060	0.060	0.010		≤ 40	Dead
			0.22						> 40
		St37-3 (1.0116)	0.19		0.050	0.050	–		All	Dead Special
European Union	EN 10025: 1993	S235JR (1.0037)	0.21	1.50	0.055	0.055	0.011		≤ 16	Optional
			0.25						16
	EN 10025-2: 2004	S235JR (1.0038)	0.19	1.50	0.045	0.045	0.014	0.60	≤ 40	Dead
			0.23						> 40

St37 steel properties

Physical properties

Material St 37-2 Density: 7.85 g/cm3
Melting Point: 1420-1460°C (2590-2660°F)

Mechanical properties

Yield strength, tensile strength, elongation and impact strength are listed in the following data sheet.

Hardness of St37-2 structural steel: ≤ 120 HBW
Impact value: ≥ 27 J, tested at room temperature 20°C (thickness: ≤ 25 mm)

Yield strength

Material Data Sheet St 37-2 – 3

	Yield limit (≥ N/mm2); Thickness (d) mm
Steel (steel number)	d≤16	16< d ≤40
St37-2 (1.0037)	235	225

Tensile strength

Material Data Sheet 1.0037 – 4

	Tensile strength (≥ N/mm2); Thickness (d) mm
Steel (steel number)	d<3	3 ≤ d ≤ 100
St37-2 (1.0037)	360-510	340-470

1MPa = 1N/mm2

Stretching

Material Data Sheet St 37-2 – 5

	Elongation (≥, %); Thickness (d), mm
Steel (steel number)	0.5 ≤d <1	1≤d <1.5	1.5 ≤d <2	2 ≤d <2.5	2.5 ≤d <3
St37-2 (1.0037)	17	18	19	20	21

	Elongation (≥, %); Thickness (d), mm
Steel (steel number)	3 ≤d ≤40	40< d ≤63	63	100 < d ≤ 150	150 < d ≤ 250
St 37-2 (1.0037)	26	25	24	22	21

Equivalent grades of St37 material

DIN 1.0037 (St37-2 material) equivalent to US ASTM AISI SAE, European EN standard, British BSI standard, French NF standard, ISO standard, Japanese JIS standard, Chinese GB standard and Indian IS standard. (For reference)

St37 Equivalent grade

German

USA

European Union

France

Japan

China

India

ISO

Standard

Steel (steel number)

Standard